Efeito do tempo de gel molar E-100 (DETDA) e E-300 (DMTDA)
No Spin Casting Mold Core Technology Is A Two-Component Gel Time Pouring System: Long Gel Time, Casting Material Can Not Be Attached In The Roll Surface, Easy Gob; Gel Time Is Short, Casting Material In The Roll Surface Has Not Yet Had Time To Spread Out It Has A Gel Form Ridges Filled Bars [4]. When The Group B Is Divided Into The Sections Selected ME-100: ME-300: MP650 = 25: 25: 50 When The Gel Longer Castable. Experimental P650 Fixed Mass Fraction Of 50 By Changing E-100 / E-300 To Change The Mass Ratio Of The Gel Time Casting, Spin Casting To Achieve The Optimum Process Conditions.
Effect Of E-100 And E-300 Mass Ratio Of Spin Casting Performance
Efeito do tempo de gel molar E-100 (DETDA) e E-300 (DMTDA)
item |
1 |
2 |
3 |
4 |
5 |
Formulation B component (parts by mass) |
|
||||
E-100 |
20 |
25 |
30 |
35 |
40 |
E-300 |
30 |
25 |
20 |
15 |
10 |
P650 |
50 |
50 |
50 |
50 |
50 |
Casting Performance |
|
||||
Gel time / s |
15 |
13 |
12 |
10 |
9 |
Package roll status |
Gob |
No tear drops, but multi-surface roughness |
No tear drops, surface roughness |
No tear drops, uneven surface |
No tear drops, the surface was shaped ridge |
Hardness / shoreA |
90 |
90 |
90 |
91 |
91 |
Increasing The E-100 And E300 Mass Ratio, The Gel Time Of The Product Is Reduced Accordingly, Drip Phenomenon Gradually Improving. This Is Because The Reaction Activity Higher Than E-100 E-300, It Is Determined Mainly By The Number Of Copies Of The E-100 Compound B Gel Time. When The Number Of Copies E-100 Is Increased To 30 Parts, Castable Gel Time Reduced To 12 S, Castable Surface Smooth, Continuous Casting The Second And Third Layer Of Polyurethane Drool Phenomenon Does Not Occur. Continue To Increase The E-100 To 40 Parts, Gel Time Is Reduced To 9 S, Castable Gel Quickly After Contacting The Roll Surface, Resulting Castable Can Not Roll Surface Flattening Roll Surface Viewed From The Outside 1 ~ 2mm Ridge Shape Uplift. Data Can Also Be Seen In The Table, Do Not Change The Amount Of P650, Only Change The Mass Ratio Of E-100 And E300, The Polyurethane Casting Had Little Effect On The Hardness.
Notícias da empresa
- Agente de reticulação de cura de poliuretano Dimetiltiotoluenodiamina (DMTDA)
- Dimetil Tiotolueno Diamina Aplicação PU Material impermeável
- EMPA Research Ajuda a Banned Flame Retardant HBCD
- Os Estados Unidos afirmam que os retardadores afetam a saúde materna
- Status de marketing retardador de chama de fosfato estrangeiro
- Retardante de chama baseado em fósforo
Notícias do setor
- Aplicação DMTDA PU Elastômeros
- Temperatura de cura e cura da resistência ao calor do agente de cura
- O que é dietiltoluenodiamina?
- Agentes de extensão de cadeia e agentes de reticulação
- Classificação de uso e aplicação de agente de cura epóxi
- Efeito do tempo de gel molar E-100 (DETDA) e E-300 (DMTDA)
Contacto
- Contatos: Sra. Shao
- sales@yaruichem.com
- Skype: yaruichem@hotmail.com
- Tel: + 86-512-58961066
- Fax: + 86-512-58961068
- QQ: 2880130940
- Endereço: RM.609A, F6, NO. 2 XINGYE RD., EDIFÍCIO JIULONG, CIDADE DE JINFENG, ZHANGJIAGANG JIANGSU, CHINA 215600